| DOI | Trouver le DOI : https://doi.org/10.1007/s11661-014-2664-8 |
|---|
| Auteur | Rechercher : Liu, Rong; Rechercher : Wu, X. J.1; Rechercher : Kapoor, Samit; Rechercher : Yao, M. X.; Rechercher : Collier, Rachel |
|---|
| Affiliation | - Conseil national de recherches du Canada. Aérospatiale
|
|---|
| Format | Texte, Article |
|---|
| Sujet | Alloys; Scanning electron microscopy; Stellite; Temperature; Tribology; Tungsten; X ray diffraction; Effects of temperature; Elevated temperature; Energy dispersive x-ray; Microhardness tester; Pin-on-disk tribometers; X-ray diffraction spectrum |
|---|
| Résumé | In this research, two new Stellite alloys containing high tungsten are developed for wear resistance application owing to the distinct beneficial effects of tungsten in Stellite alloys. The microstructures of these alloys are analyzed using a scanning electron microscope (SEM) with an EDAX energy dispersive X-ray (EDX) spectroscopy system and X-ray diffraction spectrum. The micro-hardness and wear resistance of the alloys at room temperature and at elevated temperatures are investigated utilizing a Microhardness Tester Unit, with a Hot Stage, and a Hot Pin-on-Disk Tribometer, respectively. The wear test results of these alloys are compared with those of commercial wear-resistant Stellite 3 and Stellite 12. The worn surfaces of the specimens are analyzed using SEM/EDX to explore the wear mechanisms of these alloys with temperature change. The variations of hardness and wear resistance of these alloys with temperature are studied and discussed. |
|---|
| Date de publication | 2014-11-18 |
|---|
| Dans | |
|---|
| Langue | anglais |
|---|
| Publications évaluées par des pairs | Oui |
|---|
| Numéro NPARC | 21275459 |
|---|
| Exporter la notice | Exporter en format RIS |
|---|
| Signaler une correction | Signaler une correction (s'ouvre dans un nouvel onglet) |
|---|
| Identificateur de l’enregistrement | da27f876-dd8a-43c3-8cdd-32b24f059b4c |
|---|
| Enregistrement créé | 2015-07-14 |
|---|
| Enregistrement modifié | 2020-04-22 |
|---|