Téléchargement | - Voir le manuscrit accepté : Extrusion of CO₂/n-pentane blends in polystyrene (PDF, 547 Kio)
|
---|
Auteur | Rechercher : Vachon, C.1 |
---|
Affiliation | - Conseil national de recherches du Canada. Institut des matériaux industriels du CNRC
|
---|
Format | Texte, Article |
---|
Conférence | Polymer Processing Society (PPS) Regional Meeting 2005, August 14-17, 2005, Québec, Québec, Canada |
---|
Résumé | Blends of CO₂ and n-pentane were extruded in polystyrene. Rheological characterization of the system using the on-line slit die showed that n-pentane is a more effective plasticizer than CO₂ on an equivalent molar basis. This is consistent with previous findings indicating that larger gas molecules create more internal spacing at the molecular level. Solubility and homogeneity of the blends was also probed using ultrasonic monitoring. It was observed that degassing pressure in CO₂/n-pentane blends was CO₂-dependant only. This feature enables to increase the global gas loading in a foaming system in order to improve the expansion ratio without compromising on the gas pressure exiting the die, which may cause extrusion defects. Moreover, adding a lower diffusing agent such as n-pentane is expected to decrease the overall diffusion rate of the blend. Foam characterization results revealed that incorporating n-pentane to CO₂ lowered the density further while producing foam samples comtaining virtually no open-cells as compared to its pure CO₂ counterpart. |
---|
Date de publication | 2005-01-01 |
---|
Dans | |
---|
Langue | anglais |
---|
Publications évaluées par des pairs | Non |
---|
Numéro du CNRC | NRCC 54301 |
---|
Numéro NPARC | 18399001 |
---|
Exporter la notice | Exporter en format RIS |
---|
Signaler une correction | Signaler une correction (s'ouvre dans un nouvel onglet) |
---|
Identificateur de l’enregistrement | 95f13a72-ee6b-4029-b8ac-8c151b8e3ff0 |
---|
Enregistrement créé | 2011-08-23 |
---|
Enregistrement modifié | 2020-04-07 |
---|