Téléchargement | - Voir le manuscrit accepté : DLFT experiments with cyclic butylene terephtalate (PDF, 1.5 Mio)
|
---|
Auteur | Rechercher : Bravo, Victor L.1; Rechercher : Mihalich, James; Rechercher : McLeod, Martin R.1; Rechercher : Bureau, Martin N.1 |
---|
Affiliation | - Conseil national de recherches du Canada. Automobile
|
---|
Format | Texte, Article |
---|
Conférence | 12th Annual Automotive Composites Conference & Exhibition (ACCE 2012), 11-13 September 2012, Troy, Michigan, USA |
---|
Sujet | Automotive applications; Cyclic butylene terephthalates; High molecular weight; Homogeneous mixtures; Material temperature; Poly(butylene terephthalate); Polymerization process; Processing equipment; Automobile exhibitions; Butenes; Composite materials; Glass fibers; Mechanical properties; Molecular weight; Oligomers; Polymerization; Reinforcement; Residence time distribution; Viscosity; Molds |
---|
Résumé | Cyclic oligomers have low molecular weights and therefore exhibit very low viscosities (in the order of 20 mPa.s) in contrast to the resulting high viscosities related to high molecular weightsobtained after polymerization. This characteristic is very appealing for the production of polymer composites since by taking advantage of the low viscosity, fibres can be thoroughly wetted by the cyclic oligomer before starting the reactive process of polymerization. As a result, a homogeneous mixture with a uniform volumetric distribution of reinforcing fibres in the polymer matrix is expected with the use of appropriate processing equipment. Cyclic butylene terephthalate (CBT®) has been successfully polymerized into poly(butylene terephthalate) (PBT) using a variety of tin or titanate-based initiators. An exploratory project has been initiated by NRC at the Magna-NRC Composites Centre of Excellence (MNCCE) with the participation of Cyclics Corporation (Cyclics) as the supplier of CBT for trials using the D-LFT process. The goal is to assess a number of aspects involved in the simultaneous reactive extrusion/compounding process using CBT fibreglass reinforcement in a D-LFT process in order to determine the adequate processing conditions to produce parts. This paper presents a description of the experiments conducted up to date and the results obtained thereby. Parts were produced using a test specimen mould with a shot-pot device and a storage tub for automotive applications. Samples were characterized for tensile, flexural and impact tests. Density measurements were taken at different points of the tub to examine the uniformity of the composite material obtained. Plaques moulded with the test specimen mould showed good mechanical properties which exceed typical values for PP with 40% glass composites. The experiments proved the feasibility of the use of the open ring polymerization process in a D-LFT system. A set of operating conditions including temperature profile, screw speed and feed rate was established to achieve the adequate residence time and material temperature history for the effective processing of CBT in the D-LFT system.Mechanical properties measured from the moulded part (tub) showed significantly lower values than those for the test specimen mould. These were related to incomplete packing of the material in the cavity of the mould, the high residence time required and non-optimal shot size.High variability within the parts and between parts produced is thought to be a consequence of the processing difficulties for the tub mould. |
---|
Date de publication | 2012-09-13 |
---|
Dans | |
---|
Langue | anglais |
---|
Publications évaluées par des pairs | Oui |
---|
Numéro du CNRC | NRCC 139298 |
---|
Numéro NPARC | 21047062 |
---|
Exporter la notice | Exporter en format RIS |
---|
Signaler une correction | Signaler une correction (s'ouvre dans un nouvel onglet) |
---|
Identificateur de l’enregistrement | 956ab768-30fc-4a91-b7b2-1747dea631a5 |
---|
Enregistrement créé | 2012-11-28 |
---|
Enregistrement modifié | 2020-04-21 |
---|