Téléchargement | - Voir le manuscrit accepté : Synthesis of LiNi1/3Co1/3Al1/3O2 cathode material with eutectic molten salt LiOH-LiNO3 (PDF, 838 Kio)
|
---|
DOI | Trouver le DOI : https://doi.org/10.1016/j.powtec.2010.11.025 |
---|
Auteur | Rechercher : Chang, Zhao-Rong; Rechercher : Yu, Xu; Rechercher : Tang, Hong-Wei; Rechercher : Yuan, Xiao-Zi1; Rechercher : Wang, Haijiang1 |
---|
Affiliation | - Conseil national de recherches du Canada. Institut d'innovation en piles à combustible du CNRC
|
---|
Format | Texte, Article |
---|
Sujet | Cathode materials; Eutectic molten salt; Doping; LiNi1/3Co1/3Al1/3O2 |
---|
Résumé | A lithium-ion battery cathode material, LiNi1/3Co1/3Al1/3O2, with excellent electrochemical properties was prepared by three-phase temperature sintering, using eutectic lithium salts (0.38LiOH.H2O-0.62LiNO3) mixed with the precursor Ni1/3Co1/3Al1/3(OH)2. This method was simple and inexpensive, and the materials could be mixed uniformly at the eutectic melting point without any grinding. A well-layered α-NaFeO2 structure was confirmed by X-ray diffraction (XRD). The ratio of characteristic diffraction peaks I(003)/I (104) reached 1.73. Charge–discharge testing of the synthesized powder showed an initial charge–discharge capacity of 151.5 mAh.g–1 at a specific current of 0.2 C in the range 2.8–4.3 V up to 20 cycles with no noticeable capacity-fading (94.5 percent of the first discharge capacity), and reversible capacities of 133.7 and 120.9 mAh.g–1 for specific currents of 1 C and 2 C at room temperature. The discharge capacity and capacity retention at 55 °C were substantially better than at room temperature. |
---|
Date de publication | 2010-12-03 |
---|
Dans | |
---|
Langue | anglais |
---|
Publications évaluées par des pairs | Oui |
---|
Numéro NPARC | 19542551 |
---|
Exporter la notice | Exporter en format RIS |
---|
Signaler une correction | Signaler une correction (s'ouvre dans un nouvel onglet) |
---|
Identificateur de l’enregistrement | 92ad49c7-0e2e-432b-adb3-5df5f66fdcab |
---|
Enregistrement créé | 2012-02-23 |
---|
Enregistrement modifié | 2020-04-17 |
---|