| DOI | Trouver le DOI : https://doi.org/10.1007/s10853-010-4884-7 |
|---|
| Auteur | Rechercher : Zhang, H.R.1; Rechercher : Ghoneim, A.; Rechercher : Ojo, O.A. |
|---|
| Affiliation | - Conseil national de recherches du Canada. Institut national de nanotechnologie
|
|---|
| Format | Texte, Article |
|---|
| Sujet | Brazed joint; Brazing temperature; Incipient melting; Intermetallic alloys; Microconstituents; TEM analysis; Transformation Reactions; Aluminum; Borides; Cerium alloys; Eutectics; Microstructure; Transmission electron microscopy; Brazing |
|---|
| Résumé | Transmission electron microscopy study of brazed joint microstructure in a Ni3Al-based intermetallic alloy IC 6 was performed. A continuously distributed microconstituents consisting of γ solid-solution, M 3B2-type and M23B6-type borides, which were likely formed by eutectic-type reaction(s) from residual liquated insert during cooling from brazing temperature, were observed along the joint centreline. Consideration of possible incipient melting due to eutectic-type transformation reaction of these phases is pertinent to development of post braze heat treatment for modifying the brazement microstructure. © 2010 Springer Science+Business Media, LLC. |
|---|
| Date de publication | 2011 |
|---|
| Dans | |
|---|
| Langue | anglais |
|---|
| Publications évaluées par des pairs | Oui |
|---|
| Numéro NPARC | 21272040 |
|---|
| Exporter la notice | Exporter en format RIS |
|---|
| Signaler une correction | Signaler une correction (s'ouvre dans un nouvel onglet) |
|---|
| Identificateur de l’enregistrement | 887ffadf-4b96-44e4-9c1b-fc79053a9116 |
|---|
| Enregistrement créé | 2014-05-23 |
|---|
| Enregistrement modifié | 2020-04-21 |
|---|