Solubility, diffusivity, and retrograde vitrification in PMMA-CO₂, and development of sub-micron cellular structures

Par Conseil national de recherches du Canada

Autre titreSolubility, diffusivity, and retrograde vitrification in PMMA-CO2, and development of sub-micron cellular structures
DOITrouver le DOI : https://doi.org/10.1177/026248930102000101
AuteurRechercher : ; Rechercher : ; Rechercher :
FormatTexte, Article
Résumé
A magnetic suspension balance was used to measure solubility of CO₂ in PMMA in the temperature range 0 to 167°C and at pressures to 61.2 atm. CO₂ dissolves to considerable extent in PMMA, reaching a value of about 30 wt% at 0°C and 34 atm. Diffusion coefficients, derived from the sorption kinetics, were analyzed to extract glass transition temperature of the PMMA-CO₂ system over the pressure range of 0 to about 60 atm. The results confirm the existence of retrograde vitrification in this system previously observed by creep compliance and high-pressure thermal analysis techniques. A fundamental understanding of the polymer-gas interactions has led to the development of novel, sub-micron cellular structures.
Date de publication
Maison d’éditionSage
Dans
  • Cellular Polymers 20, nº 1 : 1–16.
Publications évaluées par des pairsOui
Publication du CNRC
Cette publication n’est pas du CNRC

Ce sont des publications qui ont été rédigées par un auteur du CNRC, mais avant que celui-ci soit employé du CNRC.

Numéro NPARC12744585
Exporter la noticeExporter en format RIS
Signaler une correctionSignaler une correction (s'ouvre dans un nouvel onglet)
Identificateur de l’enregistrement719e53cb-fe82-4a72-b578-15c72534bfc0
Enregistrement créé2009-10-27
Enregistrement modifié2020-06-15
Date de modification :