| Téléchargement | - Voir le manuscrit accepté : An AES and SIMS study of the influence of chloride on the passive oxide film on iron (PDF, 809 Kio)
|
|---|
| Auteur | Rechercher : Goetz, R.1; Rechercher : MacDougall, B.1; Rechercher : Graham, M. J.1 |
|---|
| Affiliation | - Conseil national de recherches du Canada. Institut de technologie des procédés chimiques et de l'environnement du CNRC
|
|---|
| Format | Texte, Article |
|---|
| Résumé | The kinetics of passivation of Fe in pH 8.4 birate buffer solution at 0.0 V have been studied in both the presence and absence of 0.5 M Cl-. Cl- has no influence on the decay of the passive current with time over the course of several hours. Oxide films wer examined by AES and SIMS for possible Cl- incorporation into the oxide lattice. Neither technique was able to detect any Cl- within the film. The same is true even above the pitting potential, which probably indicates that Cl- incorporation into the oxide film is not a precursor to pit initiation. It also appears that Cl- does not cause any film thinning. |
|---|
| Date de publication | 1986 |
|---|
| Dans | |
|---|
| Langue | anglais |
|---|
| Publications évaluées par des pairs | Oui |
|---|
| Numéro du CNRC | NRCC 52289 |
|---|
| Numéro NPARC | 16285585 |
|---|
| Exporter la notice | Exporter en format RIS |
|---|
| Signaler une correction | Signaler une correction (s'ouvre dans un nouvel onglet) |
|---|
| Identificateur de l’enregistrement | 6aa2caa1-9105-419f-80f3-7a73c5ff82e0 |
|---|
| Enregistrement créé | 2010-11-01 |
|---|
| Enregistrement modifié | 2020-05-08 |
|---|