| DOI | Trouver le DOI : https://doi.org/10.1016/j.electacta.2012.03.108 |
|---|
| Auteur | Rechercher : Courtel, Fabrice M.1; Rechercher : Abu-Lebdeh, Yaser1; Rechercher : Davidson, Isobel J.1 |
|---|
| Affiliation | - Conseil national de recherches du Canada. Énergie, les mines et l'environnement
|
|---|
| Format | Texte, Article |
|---|
| Sujet | ZnMn2O4; Hydrothermal; Li-ion batteries; Nanoparticles; Anode material |
|---|
| Résumé | ZnMn2O4 nanoparticles prepared by a hydrothermal synthesis were evaluated as anode material for Li-ion batteries. XRD measurements showed that a ZnMn2O4 I41/amd tetragonal spinel structure was obtained with crystallite sizes ≤5 nm. TEM micrographs showed that particles of about 5 nm in diameter were synthesized. Li/ZnMn2O4 half cell battery cycling showed that the nanoparticles, using lithium salt of carboxymethylcellulose as binder, give a high capacity of 430 mAh g−¹ when cycled 100 times at C/10. |
|---|
| Date de publication | 2012-06-01 |
|---|
| Dans | |
|---|
| Langue | anglais |
|---|
| Publications évaluées par des pairs | Oui |
|---|
| Identificateur | S0013468612004604 |
|---|
| Numéro NPARC | 21268732 |
|---|
| Exporter la notice | Exporter en format RIS |
|---|
| Signaler une correction | Signaler une correction (s'ouvre dans un nouvel onglet) |
|---|
| Identificateur de l’enregistrement | 56a26879-05d0-452d-87dc-4c933ac6751f |
|---|
| Enregistrement créé | 2013-11-08 |
|---|
| Enregistrement modifié | 2020-04-21 |
|---|