| Sujet | Bulk materials; Co-doped; Doped sample; Ferroelastic toughening; Fracture toughness values; Homogeneous composition; Macroindentation; Microcrack formation; Microstructural analysis; Monoclinic phase; Optical image analysis; Porosity level; Representative sample; Sintered samples; Tetragonal phase; TiO; Volumetric porosity; XRD; XRD measurements; Young's Modulus; Blowers; Exhibitions; Geometrical optics; Marine applications; Mechanical properties; Plasma spraying; Porosity; Sintering; Thermal barrier coatings; Turbines; Titanium dioxide |
|---|
| Résumé | Representative samples of Yttria Stabilized Zirconia (7YSZ) co-doped with varying concentrations of TiO2were fabricated using plasma spraying. Samples were sintered in order to minimize porosity and to simulate the bulk material properties. After sintering, porosity levels of less than 1.25% were achieved. Both as-sprayed and sintered samples with 5, 10 and 15 wt% TiO 2 addition levels were microstructurally characterized using SEM, XRD and optical image analysis methods. Vickers hardness, Young's modulus, and fracture toughness were measured using nano and macroindentation methods. Microstructural analysis revealed that sintering of the TiO2 doped samples was required to achieve a homogeneous composition distribution, with TiO2 predominantly residing in solid solution within the ZrO2 matrix. Sintering for 325 hours at 1200 C resulted in sufficient diffusion of TiO 2 into the 7YSZ. The addition of TiO2 stabilized more tetragonal phase as revealed by XRD measurement. Sintering also showed significant improvements in fracture toughness in all co-doped samples. Fracture toughness values calculated using load-independent equations provided a clear trend in fracture toughness improvement with TiO2 addition. Ferroelastic toughening of the tetragonal phase was believed to have played an effect. There was also a reduction in monoclinic phase content with TiO 2 addition, which may have limited microcrack formation and consequently increased the fracture toughness. With the addition of 10 wt% TiO2, the fracture toughness was improved by over 50%; however, this improvement started to decline at 15 wt% TiO2 addition. Volumetric porosity measurements also revealed significant improvements in fracture toughness with respect to lowering the porosity content as observed in all sintered samples. Copyright © 2011 by ASME. |
|---|
| Date de publication | 2011 |
|---|
| Dans | |
|---|
| Langue | anglais |
|---|
| Publications évaluées par des pairs | Oui |
|---|
| Numéro NPARC | 21271499 |
|---|
| Exporter la notice | Exporter en format RIS |
|---|
| Signaler une correction | Signaler une correction (s'ouvre dans un nouvel onglet) |
|---|
| Identificateur de l’enregistrement | 3c2df9c3-4b8f-4171-8d70-2dbda331ebc5 |
|---|
| Enregistrement créé | 2014-03-24 |
|---|
| Enregistrement modifié | 2020-04-21 |
|---|