Ultrasonic measurements in sinter-forged high Tc superconductor YBa2Cu3O7-δ

Par Conseil national de recherches du Canada

DOI	Trouver le DOI : https://doi.org/10.1109/20.92793
Auteur	Rechercher : Xu, M.-F.; Rechercher : Schenstrom, A.; Rechercher : Hong, Y.; Rechercher : Bein, D.; Rechercher : Sarma, Bimal K.; Rechercher : Levy, M.; Rechercher : Zhao, Z.; Rechercher : Adenwalla, S.; Rechercher : Moreau, A.; Rechercher : Robinson, Q.; Rechercher : Johnson, D.L.; Rechercher : Hwu, S.J.; Rechercher : Poeppelmeier, K.R.; Rechercher : Ketterson, J.B.
Format	Texte, Article
Résumé	Both ultrasonic attenuation and velocity as a function of temperature from 4.2 K to room temperature were measured on sinter-forged samples of YBa2Cu3O7-δ , which have more than 80% alignment of the c-axis of the grains parallel to the forging axis. Strong anisotropy was found both in the attenuation and the velocity when propagating sound waves in different directions relative to the forging axis. Hysteresis was observed in the velocity changes.
Date de publication	1989-03
Dans	IEEE Transactions on Magnetics 25, nº 2 (mars 1989) : 2414–2417.
Langue	anglais
Publications évaluées par des pairs	Oui
Publication du CNRC	Cette publication n’est pas du CNRC Ce sont des publications qui ont été rédigées par un auteur du CNRC, mais avant que celui-ci soit employé du CNRC.
Numéro NPARC	21273105
Exporter la notice	Exporter en format RIS
Signaler une correction	Signaler une correction (s'ouvre dans un nouvel onglet)
Identificateur de l’enregistrement	235ddafe-6f07-41d4-a4c2-1eb0dc544984
Enregistrement créé	2014-12-12
Enregistrement modifié	2020-03-17

Date de modification :: 2024-04-19