High field magnetoresistance of CeAl2 at low temperatures

Par Conseil national de recherches du Canada

DOITrouver le DOI : https://doi.org/10.1016/0038-1098(86)90380-7
AuteurRechercher : ; Rechercher : 1; Rechercher : ; Rechercher : 1
Affiliation
  1. Conseil national de recherches du Canada. Institut des sciences des microstructures du CNRC
FormatTexte, Article
SujetSUPERCONDUCTING MATERIALS - Magnetic Properties; FIELD-INDUCED SUPERCONDUCTIVITY; MAGNETORESISTANCE; CERIUM COMPOUNDS
Résumé
We have measured the magnetoresistance ρ(H,T0) of the magnetic Kondo lattice CeAl2 at temperatures T0 in the range 0.035 - 1.3 K, well below the Néel temperature TN=3.8 K, in magnetic fields H up to 145 k0e. The ρ vs H curve exhibits a rapid decrease between H=45-65 kOe corresponding to the metamagnetic transition at H=HM. The resistivity then levels out to a value which depends only weakly on field and temperature. For H<HM a small positive magnetoresistance was observed with the derivative dρ/dH increasing as the temperature is lowered. The present results are compared with the ρ(H,T0) data obtained for the CePb3 magnetic Kondo lattice, where the decrease in the resistivity at H∼HM was considered earlier to be evidence of field induced superconductivity. © 1986.
Date de publication
Dans
  • Solid State Communications 60, nº 12 (1986) : 893–895.
Langueanglais
Publications évaluées par des pairsOui
Numéro NPARC21274618
Exporter la noticeExporter en format RIS
Signaler une correctionSignaler une correction (s'ouvre dans un nouvel onglet)
Identificateur de l’enregistrement211ddd25-c447-4c08-bb6d-06bc50087d7b
Enregistrement créé2015-03-18
Enregistrement modifié2020-03-17
Date de modification :