DMSO-assisted liquid-phase synthesis of LiFePO4/C nanocomposites with high-rate cycling as cathode materials for lithium ion batteries

Par Conseil national de recherches du Canada

Téléchargement
  1. (PDF, 919 Kio)
DOITrouver le DOI : https://doi.org/10.1149/1.3564875
AuteurRechercher : ; Rechercher : ; Rechercher : ; Rechercher : 1; Rechercher : 1
Affiliation
  1. Conseil national de recherches du Canada. Institut d'innovation en piles à combustible du CNRC
FormatTexte, Article
SujetNanometer-sized LiFePO4; liquid-phase method; dimethyl sulfoxide (DMSO)
Résumé
Nanometer-sized LiFePO4 was synthesized by a liquid-phase method, using dimethyl sulfoxide (DMSO) as a boiling point raiser and crystal growth inhibitor under ambient pressure, then mixed with a certain amount of glucose and sintered at 600 C under inert atmosphere for 3 h to obtain LiFePO4/C nanocomposites, which had a well developed olivine-type structure, small crystals, and a narrow size distribution. Tests showed that the special capacity of LiFePO4/C at discharge rates of 0.2 and 1 C was 157.7 and 142.5 mAh/g, respectively. A capacity of 126 mAh/g at 5 C and 104 mAh/g at 10 C was even achievable, with no significant capacity fading after 200 cycles.
Date de publication
Dans
  • Electrochemical and Solid-State Letters 14, nº 6 (22 mars 2011) : A90–A92.
Langueanglais
Publications évaluées par des pairsOui
Numéro NPARC19542550
Exporter la noticeExporter en format RIS
Signaler une correctionSignaler une correction (s'ouvre dans un nouvel onglet)
Identificateur de l’enregistrement1e84f24e-6cae-459d-ad2b-230def3cf96e
Enregistrement créé2012-02-23
Enregistrement modifié2020-04-21
Date de modification :