Ultrasonic velocity measurements during phase transformations in steels using laser ultrasonics

  1. Get@NRC: Ultrasonic velocity measurements during phase transformations in steels using laser ultrasonics (Opens in a new window)
DOIResolve DOI: http://doi.org/10.1063/1.1363681
AuthorSearch for: ; Search for: ; Search for:
Journal titleJournal of Applied Physics
Pages64876495; # of pages: 9
Subjectultrasonic velocity; phase transitions; carbon; velocity measurement; Curie point
AbstractThis article presents accurate laser-ultrasonic measurements of longitudinal velocity in the 500–1000 °C temperature range in carbon steel samples for different conditions known to affect phase transformations such as cooling rate, carbon concentration, and rolling. Measurements were performed during continuous heating and cooling at rates varying between 0.1 and 20 °C/s. Carbon concentrations ranged from 0.0% to 0.72%. Hot-rolled and cold-rolled samples were measured. For the hot-rolled samples, a reproducible hysteresis was observed in the dependence of the ultrasonic velocity versus temperature of samples having a significant carbon concentration. This hysteresis is attributed to the combined effects of the phase transformation and of the ferromagnetic–paramagnetic transition. In particular, the rate of change of velocity with temperature during heating suddenly diminishes at the Curie temperature, and the velocity behavior during cooling shows clearly the start and end of phase transformations, even allowing discrimination between ferrite and pearlite nucleations. For the cold-rolled samples, significant drops in ultrasonic velocity were observed at the transformation temperatures when the samples were heated for the first time. However, the magnitude of these drops decreased for subsequent heating. These drops are attributed to irreversible crystallographic orientation changes caused by phase transformations. This effect was modeled using the Kurdjumov–Sach transformation relationship. The model calculation agrees well with the experimental data.
Publication date
AffiliationNRC Industrial Materials Institute; National Research Council Canada
Peer reviewedYes
NPARC number21273039
Export citationExport as RIS
Report a correctionReport a correction
Record identifierdbfc76c9-8dd8-41cb-b3df-0d3c2cee3748
Record created2014-12-09
Record modified2016-05-09
Bookmark and share
  • Share this page with Facebook (Opens in a new window)
  • Share this page with Twitter (Opens in a new window)
  • Share this page with Google+ (Opens in a new window)
  • Share this page with Delicious (Opens in a new window)
Date modified: