Effect of Testing Temperature on Shear Tensile Properties of a Friction Stir Lap Welded AZ31B-H24 Magnesium Alloy

AuthorSearch for: ; Search for: ; Search for: ; Search for:
ConferenceConference of Metallurgists, September 28-October 2, 2014, Vancouver, Canada
SubjectFrictions stir lap welding; Magnesium alloy; Shear property; Testing temperature
AbstractIn this study, 2-mm thick AZ31B-H24 Mg alloy sheets were friction stir welded in a lap joint configuration at different tool rotational rates (1000 and 1500 rpm) and welding speeds (10 and 20 mm/s). The tensile behavior of these lap joints was then evaluated at low (-40°C), room (25°C), and elevated (180°C) temperatures. The room temperature mechanical behavior indicated that the tensile failure load increased with decreasing heat input, i.e. decreasing tool rotational rate and increasing welding speed, such that a maximum failure load was obtained for operational conditions of 1000 rpm and 20 mm/s. This tendency in the failure load was also apparent for all the temperatures tested in this work. Compared to the room temperature condition, however, the fracture strengths decreased at both low and high temperatures, probably due to the relatively brittle and ductile behaviors demonstrated, respectively. The fracture modes were further detailed by using fractographic analysis.
AffiliationAerospace; National Research Council Canada
Peer reviewedYes
NPARC number21276103
Export citationExport as RIS
Report a correctionReport a correction
Record identifierd66ef13a-a193-4afc-8db7-8cbcbcd9c32a
Record created2015-09-23
Record modified2016-05-09
Bookmark and share
  • Share this page with Facebook (Opens in a new window)
  • Share this page with Twitter (Opens in a new window)
  • Share this page with Google+ (Opens in a new window)
  • Share this page with Delicious (Opens in a new window)
Date modified: