Electroluminescence and photoluminescence from Si1-xGex alloys grown on (100) silicon by molecular beam epitaxy

  1. Get@NRC: Electroluminescence and photoluminescence from Si1-xGex alloys grown on (100) silicon by molecular beam epitaxy (Opens in a new window)
DOIResolve DOI: http://doi.org/10.1016/0921-5107(91)90179-Y
AuthorSearch for: ; Search for: ; Search for:
Journal titleMaterials science and engineering: B
Pages237244; # of pages: 8
AbstractPhotoluminescence has been observed from Si1−xGex alloy layers, superlattices and non-periodic multilayers where x was varied from 0 to 0.6 A p-type Si0.82Ge0.18 alloy layer 200 nm thick, grown by molecular beam epitaxy (MBE), has been fabricated into a mesa diode which operated as a light-emitting diode, emitting at 1.4 μm at temperatures up to 80 K. This diode was selected from a series of heterostructures which exhibited intense photoluminescence with internal quantum efficiencies in the range 1%–10% at low temperatures. Photoluminescence in the wavelength range 1.2–1.7 μm has been observed from thick (100–200 nm) Si1−xGex alloys and Si1−x−Si strained layer superlattices with a range of dimensions which was large compared with the unit cell; i.e. where Brillouin zone folding effects were negligible. The intense Si1−xGex alloy photoluminescence peak had a halfwidth of about 80 meV and the peak energy was found to shift consistently and predictably with the germanium fraction. Photoluminescence peak energies at 4.2 K varied from 620 to 990 meV for germanium fractions where 0.53 >x > 0.06. The photoluminescence and electroluminescence peaks were consistently about 120 meV below the established bandgap for tetragonally strained Si1−xGex. In general, Si1−xGex strained layers grown at low temperatures typical of MBE (below 500°C) exhibited low photoluminescence intensity. However, post-growth annealing in the 500–700°C temperature range enhanced luminescence efficiency by up to two orders of magnitude. A comparison is also made of the broad intense photoluminescence observed from MBE material with the weak near-band-edge spectra obtained from Si1−xGex-Si grown by low temperature chemical vapour deposition.
Publication date
AffiliationNational Research Council Canada; NRC Institute for National Measurement Standards; NRC Institute for Microstructural Sciences
Peer reviewedNo
NRC number1148
NPARC number8898384
Export citationExport as RIS
Report a correctionReport a correction
Record identifierc85b0ead-e0eb-4f0e-b96d-13cd1a791118
Record created2009-04-22
Record modified2016-05-09
Bookmark and share
  • Share this page with Facebook (Opens in a new window)
  • Share this page with Twitter (Opens in a new window)
  • Share this page with Google+ (Opens in a new window)
  • Share this page with Delicious (Opens in a new window)
Date modified: