Cold spray forming Inconel 718

AuthorSearch for: ; Search for: ; Search for: ; Search for: ; Search for: ; Search for: ; Search for: ; Search for:
Proceedings titleThermal Spray 2012: Proceedings from the International Spray Conference and Exposition
ConferenceInternational Thermal Spray 2012 Conference and Exposition (ITSC 2012), May 21-24, 2012, Houston, Texas, USA
Pages243248; # of pages: 6
AbstractIn this investigation, Inconel 718, a material known to cause nozzle clogging upon cold spraying, was cold spray formed to 6 mm-thick using the Plasma Giken cold spray system PCS- 1000. This was made possible due to the novel non-clogging nozzle material combined with a nozzle water cooling system. Coatings were as-spray formed using both nitrogen and helium as the propelling gasses. The resulting microstructures as well as the corresponding mechanical properties were studied. In addition, the effect of post-heat treatments was also investigated. It was found that for a given propelling gas used, the coating porosity level remained relatively similar (about 2.4% for nitrogen and 3.6% for helium) regardless of the coating treatment (as-sprayed or heat treated). Visual inspection from SEM micrographs showed a higher fraction of inter-particle metallurgical bonds for nitrogen gas sprayed coatings heat treated at 1250°C for 1 hour due to some sintering effect. This significantly affected its tensile properties with an average resulting ductility of 24.7%.
Publication date
AffiliationNational Research Council Canada; Automotive
Peer reviewedYes
NRC number139268
NPARC number21047057
Export citationExport as RIS
Report a correctionReport a correction
Record identifierc1af9ca4-47c1-4cc0-91b7-add039b3d759
Record created2012-11-28
Record modified2016-05-27
Bookmark and share
  • Share this page with Facebook (Opens in a new window)
  • Share this page with Twitter (Opens in a new window)
  • Share this page with Google+ (Opens in a new window)
  • Share this page with Delicious (Opens in a new window)
Date modified: