Fretting behavior of cold-sprayed Cu and Cu-MoS2 coatings

AuthorSearch for: ; Search for: ; Search for: ; Search for: ; Search for:
Proceedings titleProceedings from the International Thermal Spray Conference
ConferenceThermal Spray 2015: Proceedings from the International Thermal Spray Conference, May 11-14, 2015, Long Beach, California, USA
Pages420426; # of pages: 7
AbstractCu and Cu-MoS2 coatings were fabricated by cold gas dynamic spray and the fretting wear performance of the two coatings was compared. A mixture (95 wt.% Cu + 5 wt.% MoS2) was used as feedstock for the composite coating. Coatings were sprayed with identical gas flow conditions on the substrates preheated to approximately 170°C. The cross section of the coatings was analyzed by scanning electron microscope (SEM) and MoS2 concentration was measured, as well as coating microhardness. Fretting tests were carried out under gross slip conditions in ambient environment. SEM observation on wear scars and counterspheres revealed the development of third bodies, by which the sliding was accommodated. For the Cu-MoS2 coating, solid lubrication effects in the form of friction drops occurred in early cycles (< 5k), but eventually (> 5k) the coating's friction behavior was similar to the pure Cu coating. Third body morphology and wear of the two coatings were distinctly different, which could largely be attributed to the hardness reduction of the Cu-MoS2 composite due to poorly bonded interfaces induced by the effect of MoS2 during particle impact and coating formation.
Publication date
AffiliationAutomotive and Surface Transportation; National Research Council Canada
Peer reviewedYes
NPARC number21275335
Export citationExport as RIS
Report a correctionReport a correction
Record identifierbd57a8a6-c96e-41ca-bd6c-582dc96e2d27
Record created2015-06-11
Record modified2016-05-09
Bookmark and share
  • Share this page with Facebook (Opens in a new window)
  • Share this page with Twitter (Opens in a new window)
  • Share this page with Google+ (Opens in a new window)
  • Share this page with Delicious (Opens in a new window)
Date modified: