Ultrasonic absorption in ultra-low carbon steel

  1. Get@NRC: Ultrasonic absorption in ultra-low carbon steel (Opens in a new window)
DOIResolve DOI: http://doi.org/10.1063/1.1593220
AuthorSearch for: ; Search for:
Journal titleJournal of Applied Physics
Pages37713780; # of pages: 10
Subjectabsorption spectra; carbon; thermoelasticity; ultrasonics; internal friction
AbstractThe laser-based reverberant technique is used to measure ultrasonic absorption spectra in the 2 to 45 MHz frequency range. This technique, being contactless, allows measurements at high temperature. The absorption spectra of ultra-low carbon steel samples are studied at room temperature in a magnetic field (in order to suppress the magnetoelastic contribution) and in a high temperature furnace(20–1200 °C) without magnetic field. Small steel samples (about 10×10×1 mm3) are used. At room temperature, two main contributions to the ultrasonic absorption are identified: microeddy currents (magnetoelastic contribution) and absorption caused by dislocations (deformation contribution). A typical microeddy current peak is observed and yields a reasonable estimate of the magnetic domain size. Above 10 MHz, the nonmagnetic contribution to the total absorption follows the classical vibrating string model. However, other phenomena also contribute to the absorption spectra. Below 10 MHz, an amplitude-independent damping background is observed. In addition, a small frequency-independent contribution to the absorption is observed at room temperature and is attributed to a thin surface layer. The absorption at high temperature is dominated below the Curie point by the magnetoelastic contribution. Two internal friction peaks are also detected. The first one, at 100 °C, is related to the dislocation kink motion. The second one, measured at 330 °C and 10 MHz, is attributed to the Snoek relaxation of carbon and/or nitrogen in α-iron. The Curie transition as well as the ferrite-austenite transition strongly affect the internal friction spectra.
Publication date
AffiliationNRC Industrial Materials Institute; National Research Council Canada
Peer reviewedYes
NPARC number21273003
Export citationExport as RIS
Report a correctionReport a correction
Record identifierafbb57a5-f505-40e1-8fa8-2e70c4058ed6
Record created2014-12-05
Record modified2016-05-09
Bookmark and share
  • Share this page with Facebook (Opens in a new window)
  • Share this page with Twitter (Opens in a new window)
  • Share this page with Google+ (Opens in a new window)
  • Share this page with Delicious (Opens in a new window)
Date modified: