Investigating the Cause of Blistering in SBS Polymer Modified-Bitumen Roofing Membranes

  1. (PDF, 4 MB)
DOIResolve DOI:
AuthorSearch for: ; Search for:
TypeTechnical Report
Series titleInternal Report (National Research Council Canada. Institute for Research in Construction); no. IRC-IR-759
Physical description39 p.
SubjectRoofs; Roofs
AbstractThe cause of blistering in modified bituminous roofing membrane systems was investigated. Membrane samples were removed from several existing modified bituminous roofs containing blisters. Their mechanical behaviour was characterized by tensile tests. Gas content within the blisters were collected in canisters in the field and their chemical composition was determined quantitatively by Gas Chromatography /Mass Spectroscopy (GC/MS). Mechanical testing indicates that blister formation does not seem to depend onthe strength of the modified bituminous membrane. Also, the existence of blisters did not reduce the strength of the membrane, at least not where the blister remained intact. GC/MS revealed that the gas within the blisters was composed mainly of air and water vapour, with a negligible amount of volatile organic compounds. The relative humidity of the blister gas ranged from 30 to 75%. These findings indicated that the mechanism of blister formation and growth in modified bituminous roofs is possibly the same as that inbuilt-up roofing where water vapour promotes blister growth by exerting cyclic pumping action to the blister following the diurnal changes in temperature.
Publication date
PublisherNational Research Council Canada
AffiliationNRC Institute for Research in Construction; National Research Council Canada
Peer reviewedNo
NRC numberNRC-IRC-8199
NPARC number20331503
Export citationExport as RIS
Report a correctionReport a correction
Record identifier770bed80-ec9d-46e1-8823-78a001cde2fb
Record created2012-07-18
Record modified2017-06-14
Bookmark and share
  • Share this page with Facebook (Opens in a new window)
  • Share this page with Twitter (Opens in a new window)
  • Share this page with Google+ (Opens in a new window)
  • Share this page with Delicious (Opens in a new window)
Date modified: