Structure and Properties of Melt-Spun PET/MWCNT Nanocomposite Fibers

  1. (PDF, 1 MB)
  2. Get@NRC: Structure and Properties of Melt-Spun PET/MWCNT Nanocomposite Fibers (Opens in a new window)
DOIResolve DOI:
AuthorSearch for: ; Search for: ; Search for:
Journal titlePolymer Engineering and Science
Pages19561968; # of pages: 13
Subjectpolyethylene terephthalate; melt-spun fibers; carbon nanotubes; microfibers
AbstractPolyethylene terephthalate (PET) melt-spun fibers were modified with multiwall carbon nanotubes (MWCNT) to obtain conductive microfibers smaller than 90 lm in diameter. Physical properties such as crystallinity and orientation of as-spun fibers were studied by X-ray diffraction, Raman spectroscopy, and microscopy techniques at different draw ratios (DR) and MWCNT concentrations. Morphological and orientation analysis of MWCNT after melt-spinning process showed agglomerates formation and highly oriented CNTs. The study of the orientation of PET crystalline phase in drawn fibers proved that the addition of nanoparticles decreases the orientation of crystalline units inside the fibers. The orientation of MWCNT as well as that of PET chains was studied using Raman spectroscopy at different DR and a high degree of CNT orientation was observed under high DR conditions. Mechanical and electrical properties of as-spun fibers were also investigated. Our results showed that it was possible to achieve conductive fibers at a MWCNTconcentration of 2% w/w, and more conductive fibers using higher DR were also obtained without increasing the MWCNT concentration. Mechanical properties results showed interestingly high value of maximum tensile strain at break (emax) of nanocomposite fibers, up to three times more than pure PET fibers.
Publication date
AffiliationNRC Industrial Materials Institute; National Research Council Canada
Peer reviewedYes
NRC number53859
NPARC number16919794
Export citationExport as RIS
Report a correctionReport a correction
Record identifier74bf8693-9715-404f-b628-c0afac9e8fc4
Record created2011-03-07
Record modified2016-05-09
Bookmark and share
  • Share this page with Facebook (Opens in a new window)
  • Share this page with Twitter (Opens in a new window)
  • Share this page with Google+ (Opens in a new window)
  • Share this page with Delicious (Opens in a new window)
Date modified: