Synthesis, cross-linking and carbonization of co-polyimides containing internal acetylene units for gas separation

  1. (PDF, 621 KB)
  2. Get@NRC: Synthesis, cross-linking and carbonization of co-polyimides containing internal acetylene units for gas separation (Opens in a new window)
DOIResolve DOI:
AuthorSearch for: ; Search for: ; Search for: ; Search for:
Journal titleJournal of Membrane Science
Pages254264; # of pages: 11
SubjectGas separation; Co-polyimide; Cross-linking; Carbonization; Membranes
AbstractCross-linkable polyimides containing internal acetylene units have been synthesized by random copolymerization of 6FDA dianhydride, 2,3,5,6-tetramethyl-1,4-phenylenediamine (Durene) and 4,4′-diaminodiphenylacetylene (p-intA) diamine as materials for gas separation. Compared with 6FDA-Durene polyimide, 6FDA-Durene/p-intA co-polyimide shows denser polymer chain packing, which is confirmed by wide-angle X-ray diffraction (WAXD). The thermally treated co-polyimides are insoluble in various solvents and show an increase in Tg, indicating the formation of network structures among the polymer chains. Differential scanning calorimetry (DSC) and FT-Raman suggest that cross-linking arises from Diels-Alder cycloaddition between the internally arranged acetylene units along the polymer main chain, resulting in extended conjugated aromatic structures. The thermally cross-linked membranes show enhanced resistance to CO2 plasticization up to around 5 × 106 Pa (700 psi). The rigidified membrane structure provides increased gas selectivity without severely compromising gas permeability. The gas separation performance of carbonized membranes is remarkably superior to those of neat and cross-linked copolyimides because of a large increase in rigidification in the polymer matrix. A Diels-Alder cycloaddition reaction produces a much more rigid and planar conjugated aromatic structure in the polymer chains and results in a higher degree of graphitization during carbonization, which is confirmed by XPS and WAXD. Carbon membranes derived from co-polyimides with more internal acetylene units show much better gas separation performance than those derived from polyimides without internal acetylene units.
Publication date
AffiliationNational Research Council Canada; NRC Institute for Chemical Process and Environmental Technology
Access conditionavailable
Peer reviewedYes
NRC number49125
NPARC number8925788
Export citationExport as RIS
Report a correctionReport a correction
Record identifier3c3b7838-c577-4176-bed5-ea23e21890a4
Record created2009-04-23
Record modified2016-05-09
Bookmark and share
  • Share this page with Facebook (Opens in a new window)
  • Share this page with Twitter (Opens in a new window)
  • Share this page with Google+ (Opens in a new window)
  • Share this page with Delicious (Opens in a new window)
Date modified: